GaAs tip_bias_mode OxideLayer LateralPFM plastics PinpointPFM Multiferroic_materials pinpoint mode HACrystal Worcester_Polytechnic_Institute ItoGlass AmplitudeModulation Optical Sio2 Dr.JurekSadowski Kevlar TungstenThinFilmDeposition domain_switching Pinpoint PFM HumanHair Ferrite temperature controller AFM molecule Molybdenum_disulfide I-VSpectroscopy LiNbO3 cross section SiliconeOxide ULCA FAFailureAnlaysis MechanicalProperties IRDetector Domain hard_disk Hafnium_dioxide
Report image
If you found this image unacceptable, please let us know. We will review your report and take action if we determine this image is really unacceptable.
Collagen film phase change by temp
Scanning Conditions
- System: NX10
- Scan Mode: Tapping
- Cantilever: AC160TS
- Scan Size: 20μm×20μm, 1μm×0.5μm
- Scan Rate: 0.3Hz for 20µm×20µm scan, 1Hz for 1µm×0.5µm scan
- Pixel: 512 × 256 for 20µm×20µm scan, 256 × 128 for 1µm×0.5µm scan
- Scan Mode: Tapping
- Cantilever: AC160TS
- Scan Size: 20μm×20μm, 1μm×0.5μm
- Scan Rate: 0.3Hz for 20µm×20µm scan, 1Hz for 1µm×0.5µm scan
- Pixel: 512 × 256 for 20µm×20µm scan, 256 × 128 for 1µm×0.5µm scan