Full Scale Wafer Analysis by Imaging Ellipsometry and Ellipsometric Contrast Micrography (ECM)

S. Funke, P. Braeuninger -Weimer, P. H. Thiesen, S. Hoffmann

Imaging Ellipsometry

Imaging ellipsometry, combines the power of ellipsometry with optical microscopy. It achieves the highest lateral resolution in the field of ellipsometry and offers a very sensitive imaging technology for thin films. Typical samples range from tiny samples like flakes of 2D materials to inhomogeneous surfaces like some CVD grown samples of 2D materials or terraces at epitaxial Graphene surfaces.

app08 fig01


The ep4 is the latest microscopic imaging spectroscopic ellipsometer with unique measurement capabilities. It can provide real-time ellipsometric enhanced contrast images, and maps of the ellipsometric angles Δ and Ψ . These data can be transferred into Thickness and the complex refractive indices by computerized optical modeling.

 

app05 fig02 new

 

ECM – Contrast Mode

 

The standard setup of an imaging ellipsometer: The lens system and CCD offer a microscopic view on the sample.
With the polarizer (P), compen-sator (C) and analyzer (A) a full control of the state of polarization of the incoming light and light after reflection
and interaction with the sample is given. The rotation of P, C, A may change the contrast in the view as it is shown in b and c. The only difference
between the two images are the rotational angles of P and A.

app09 fig02

 

 

Ellipsometry Mode

 

 

For the ellipsometry mode contrast images are taken for different rotational angles of
P, C, A in order to determine the change in the state of polarization, that is induced by the sample.
It is expressed in Δ/Ψ. From the stack of intensity images, micromaps of Δ/Ψ are calculated.
The micro-maps can be modeledwith an optical model (layerstack of materials) to thickness and refractive index maps. An example of a thickness map of Graphene on a SiO2 layer is shown on the right.

app09 fig03 

 

Optical Properties of MoS2/WSe2

 

 

a): The ellipsometric enhanced contrast micrograph and the layer structure used for the final modelling.
Conventional microscopy can hardly distinguish between monolayers and substrates.
b): An exemplary Psi map at 410 nm with the regions used for extracting Delta and Psi spectra (right) in the range of 400 nm – 800 nm.
The resulting dispersions for all regions are shown in
c). The measurement and analysis is done simultaneously for all regions

app09 fig04

ECM Compared to Other Methods

 

a): The same region of Graphene on 300 nm SiO2 measured by Raman-mapping, Optical Microscopy (OM),
Ellipsometry Mode and ECM mode and their measurement time.

b): The histogram of each method shows best distinguishing for the ellipsometry mode.
The numbers indicate the layer number of Graphene. The higher the distance in-between 2 peaks,
the better the method is able to distinguish the layer numbers.

 app09 fig05

 

Graphene on Copper

a): ECM stitching obtains a large sample overview. False coloring according to layer number as depicted
in the histogram. For the overview ECM images are recorded with an motorized XY-stage and
stitched seamlessly. The histogram can be used to calculate layer coverage ratios.
In figure b) another comparison of OM and ECM is shown. The different regions of stacked
2D materials can be hardly distinguished in the OM (left) image, but very well in the ECM Image on the right.

app09 fig06 

Graphene on Cu-foil as Grown

a): ECM stitching obtains a large sample overview. False coloring according to layer number as depicted in the histogram. For the overview ECM images are recorded with an motorized XY-stage and stitched seamlessly. The histogram can be used to calculate layer coverage ratios. In figure b) another comparison of OM and ECM is shown. The different regions of stacked 2D materials can be hardly distinguished in the OM (left) image, but very well in the ECM Image on the right.

app09 fig07

Further investigations at the flipped contrasts are done. Figure c) shows a Graphene hexagon with two different regions (flipped and non-flipped contrast). Spectroscopic imaging ellipsometry measurements are done for the Regions of interest (ROI) shown in grey shapes in the Ψ map. The resulting spectra are shown in d). The optical modeling yields the refractive indices for the Copper, Graphene and the Copper-oxide (figure e)). The contrast flip is not induced by the curvature of the foil, but by the partial oxidation of the Copper.

app09 fig08

Full 4“ Wafer Scan

 

app09 fig09

The figure above shows a 4” native – Silicon wafer, that is partially covered with Graphene monolayer. Conventional method for fast analysis are not able to distinguish Graphene monolayer on native Silicon, but ECM is. The complete scan is done within 47 minutes and reveals defects, contaminations and cracks as small as 10 µm.